GC Gold Label 2 Lc (Light-Cured)

Features

Smaller particles
Excellent aesthetics and polishability
Higher filler loading
Significantly improved abrasion resistance
Good radiopacity
Facilitating post-operative diagnosis
Self-adhesive to tooth structure
No etching, no bonding
Hydrophilic
Very good results in areas where rubber dam is difficult to use, cavity margins are in dentin and enamel prisms can not be properly etched
Smooth, porosity-free surface after sealing with GC G-Coat Plus
Practical application and manipulation
Available in 11 translucent VITA shades
Excellent aesthetics

Description

Light-Cured Reinforced Glass Ionomer Restorative – Resin reinforcement and light curing enhances physical and aesthetic properties making Gold Label 2LC one of GC’s top-of-the-line glass ionomer restorative.

GC Fuji II LC Improved is the world-wide leading light-cured glass ionomer cement. Although designed primarily as a restorative material for use in Class III, V and deciduous teeth, GC Fuji II LC Improved is a multipurpose material, with secondary indications such as liner, base and core build-up.

A Strontium-based Glass Ionomer:

All GC Gold Label Glass Ionomer contains strontium glass. The strontium glass provides good radiopacity and snapset characteristics, unanimously preferred by clinicians around the world. Interestingly, strontium will mimic calcium in the formation of strontium hydroxyapatite and strontium fluoroapatite to affect internal remineralization within the tooth structure.

Surface Strengthening Effect:
Research has shown that a strontium-based glass ionomer placed in calcium-containing environment (saliva) will result in calcium ion diffusing into the glass ionomer surface achieving a surface strengthening effect. All GC Gold Label Glass Ionomer strengthens over time in saliva.

A Consistent Predictable Seal:
All GC Gold Label Glass Ionomer will display a glossy surface after mixing. This indicates sufficient free polyacrylic acid is available to begin the ion exchange process. The subsequent movement of ions between dentin, enamel and GC Glass Ionomer creates an ion exchange zone which chemically fuses them together. The resulting seal is consistent, predictable and long lasting.

INDICATIONS

Class III and V restorations, particularly for cervical erosions and root surface caries
Restoration of primary teeth
Core build up
Cases where radiopacity is required
Geriatric applications
As a base or liner.

CONTRAINDICATIONS

Pulp capping
In rare cases the product may cause sensitivity in some people. If any such reactions are experienced, discontinue the use of the product and refer to a physician

ADVANTAGES:

Allows minimal cavity preparation
Less stress on margins and marginal seal
Protects against secondary caries
Excellent esthetics and finish
Improved abrasion resistance
Allows for immediate finishing after light curing while ensuring total material set
Ease of colour match to tooth shade
More durable, longer lasting restorations
Assurance of successful restorations

Specifications

TECHNICAL DATA:

Powder / Liquid Ratio (g/g):3.2 / 1.0
Mixing Time (sec.):20-25 secs
Working Time (min., sec.): 3 mins45 secs
Light Curing Time (sec.):20 secs
Depth of Cure (A2) (mm):1.8

Gc Gold Label 2 Lc Mini Pack Shade A2:

1 x 5g Powder
1 x 3g (2.6ml) Liquid

Gc Gold Label 2 Lc 15G Powder Shade A2:

1 x 15g Powder

Gc Gold Label 2 Lc 1-1 Pkg Shade A2:

1 x 15g Powder
1 x 8g Liquid

Directions For Use

1. POWDER AND LIQUID DISPENSING

a) Select shade based on Vita shade guide. : Vita is a registered trademark of Vita Zahnfabrik, Bad Säckingen, Germany

b) The standard powder to liquid ratio is 3.2g / 1.0g. 1 level scoop of powder to 2 drops of liquid

c) For accurate dispensing of powder, tap the bottle gently. Do not shake or invert

d) Hold the liquid bottle vertically and squeeze gently

e) Close bottles immediately after use

2. MIXING

a) Fluff powder of bottle before dispensing

b) Place one scoop of powder and two drops of liquid on pad. Divide powder in half

c) Spread liquid out into a thin layer (about the size of a half dollar or 3 cm) with plastic spatula

d) Pull half of the powder onto liquid and mix with lapping strokes (like impression material) for 10 to 15 seconds

e) Pull in remaining powder and mix thoroughly to a glossy consistency. Do not exceed 20-25 second total mixing time

3. RESTORATIVE TECHNIQUE

a) Prepare tooth using standard techniques. Extensive mechanical retention is not necessary. For pulp capping use calcium hydroxide

b) Apply GC CAVITY CONDITIONER (10 seconds) or GC DENTIN CONDITIONER (20 seconds) to the bonding surfaces using a cotton pellet or sponge

c) Rinse thoroughly with water. Dry by blotting with a cotton pellet or gently blowing with an air syringe. DO NOT DESICCATE. Best results are obtained when prepared surfaces appear moist (glistening)

d) Mix the required amount of cement. Working time is 3 minutes 45 seconds from the start of mixing at 23°C (73.4°F). Higher temperatures will shorten working time

e) Transfer cement to the preparation using a syringe or suitable placement instrument. Avoid air bubbles

f) Form the contour and place a transparent matrix if required

g) Light cure for 20 seconds using a visible light curing device (470 nm wavelength). Place light source as closely as possible to the cement surface. Note : For cavities deeper than 1.8 mm, use a layering technique

4. FINISHING

Remove matrix and finish under water spray using standard techniques. Note : Apply a final coat of GC Fuji VARNISH (blow dry) or GC Fuji COAT LC (light cure for 10 sec.) or G-COAT PLUS (light cure for 20 sec.).