Dentsply Ah Plus Root Canal Sealant

Features

Radio opacity

Depending on the condensation technique used, thicker layers (master point technique) down to very thin layers (lateral condensation technique) can be achieved. In order to ensure adequate visibility of the filling material even in these thin layers, the radio-opacity has further been increased in AH Plus. This was possible due to using new fillers with a greater absorption capacity.

Shrinkage, Solubility, and Expansion

The main objective of this AH Plus root canal filling is to achieve a high degree of tightness. The quality of the root canal filling directly depends on the shrinkage upon setting and the solubility of the material used, as these properties are decisive for the impermeability of the treated root canal.

Film Thickness

AH Plus has a film thickness of 26µm, which is clearly below the value of less than 50µm required by the ISO standard for root canal sealing materials.

Flow Behavior

The flow behavior of dental material is one of the most important handling properties. Firstly, favorable flow behavior results in easy mixing. Secondly, the filling material must be able to be introduced easily into the root canal and exhibit a certain stability there. Therefore, AH Plus has been designed to be slightly thixotropic. A flow of 36 mm also perfectly meets the requirements of the ISO standard (> 25 mm).

Sealing Abilities

AH Plus has an excellent ability to seal root canals and make them impermeable.

Adhesion to dentin

It gets easily adhered to the dentine and results in reducing the risk of root canal microleakage and maintaining a cohesive filling mass.

Description

Dentsply AH Plus Root Canal Sealing Material is a two-component paste/paste root canal sealer based on epoxy-amine resin. The AH Plus sealer shows extremely low shrinkage making it a suitable choice of material to seal the root canal.

It is a good sealer choice for use with ProTaper Thermafil obturators as the setting reaction is not adversely affected by thermoplastic obturation.

Indications

AH Plus sealer can be used in conjugation with obturating material to establish an adequate seal of the root canal system.

Advantages

This root canal sealer can be used with hot or cold obturation technique.

Achieves a tight seal

Self-adhesive properties

Dimensional stability

Excellent biocompatible

Exhibits moderate antimicrobial properties

Extremely radio-opaque so it is clearly visible on radiographs

Specifications

Composition

AH Plus Paste A	AH Plus Paste B
Bisphenol-A epoxy resin	Dibenzyldiamine
Bisphenol-F epoxy resin	Aminoadamantane
Calcium tungstate	Tricyclodecane-diamine
Zirconium oxide	Calcium tungstate
Silica	Zirconium oxide
Iron oxide pigments	Silica
	Silicone oil

Caution

Do not exchange caps of tubes. The colored cap belongs to the colored tube; the white cap belongs to the white tube.

Working Time

The working time is at minimum 4 hours at 23 °C .

Setting Time

The setting time is at minimum 8 hours at 37 °C .

1 x 4ml Paste A
1 x 4ml Paste B

Directions For Use

STEP 1

Preparation of the Root Canal
Prior to the application of AH Plus, prepare, clean, and dry the root canals to be filled using state-of-the-art endodontic techniques.

STEP 2
Dosage and Mixing
Using AH Plus in tubes: Mix equal volume units (1:1) of Paste A and Paste B on a glass slab or a mixing pad using a metal spatula.
Mix to a homogeneous consistency.